Properties |
|
Test Method |
|
Unit |
|
2210J |
|
|
|
|
Melt Flow Rate (MFR) 190℃ |
ASTM D-1238 |
g/10min |
7.0 |
|
|
|
|
Mold Shrinkage |
HPC Method |
% |
1.8 |
|
|
|
|
Density2 |
ASTM D-1505 |
g/㎤ |
0.959 |
|
|
|
|
Softening Point |
ASTM D-1525 |
℃ |
122 |
|
|
|
|
Tensile Strength at Yield |
ASTM D-638 |
Kg/㎠ |
240 |
|
|
|
|
Ultimate Elongation |
ASTM D-638 |
% |
>300 |
|
|
|
|
Heat Distortion Temperature(4.6㎏/㎠) |
ASTM D-648 |
℃ |
75 |
|
|
|
|
Flexural Modulus of Elasticity |
ASTM D-790 |
Kg/㎠ |
12,000 |
|
|
|
|
Hardness(Rockwell) |
ASTM D-785 |
R |
64 |
|
|
|
|
Du-Pont Impact Strength(23℃) |
HPC Method |
㎏·㎝ |
90 |
|
|
|
|
IZOD Impact Strength (23℃) |
ASTM D-256 |
Kg·cm/cm |
10 |
|
|
|
|
ESCR |
ASTM D-1693 |
F 50HR |
6 |
|
|
|
|
|