FE 0070

/ / / / /

LG CHEM

FE 0070

Back to prev.

LUTENE-H FE0070

HDPE : Film Extrusion Molding Grade

Application

Merchandise bag,consumer trash bag, liner.

Feature

LUTENE-H FE0070 is mainly intended for extrusion of blown film with high mechanical properties for the manufacture of "T-Shirt" grocery sacks, can liners. Especially, LUTENE-H FD0070 resin can be relied upon for excellent performance under heavy load conditions. LUTENE-H FD0070 resin is a high molecular weight, high density polyethylene. The film produced from this resin characteristically exhibits high tensile strength, stiffness, impact strength and barrier properties. It can be down-gauged to as low as 10㎛.

Properties

Physical	Method	Condition	Unit	Value
Melt Index	ASTM D1238	190℃/2.16kg	g/10min	0.05
Melting Temperature	DSC	10℃/min	℃	133
Density	ASTM D792	23℃	g/㎤	0.953

Thermal	Method	Condition	Unit	Value
Vicat Softening Point	ASTM D1525	1kg	℃ ℉	128 262.4

Film Charateristics	Method	Condition	Unit	Value
Tensile Strength at Yield	ASTM D882	MD	kg/㎠ MPa psi	360 35.5 5119.2
Tensile Strength at Yield	ASTM D882	TD	kg/㎠ MPa psi	380 37.5 5403.6
Tensile Strength at Break	ASTM D882	MD	kg/㎠ MPa psi	590 58.2 8389.8
Tensile Strength at Yield	ASTM D882	TD	kg/㎠ MPa psi	610 60.2 8674.2
Elongation at Break	ASTM D882	MD	%	640
Elongation at Break	ASTM D882	TD	%	540
Tear Strength	ASTM D1922	MD	g	100
Tear Strength	ASTM D1922	TD	g	22
Dart Impact Resistance	ASTM D1709	-	g	240
Film Thickness	-	-	㎛	30

1) The listed values should be used for referential purpose only.