LUTENE-H BE0400 |
|
HDPE : Blow Molding Grade |
|
|
|
Blow molded containers with capacities ranging a few milliliters up to 20 liters,sheet |
|
LUTENE-H BE0400 is an excellent material for blow-molded articles with high density and rigidity. It has good flow characteristics and impact resistance. |
|
Physical |
Method |
Condition |
Unit |
Value |
|
Melt Index |
ASTM D1238 |
190℃/2.16kg |
g/10min |
0.25 |
|
Melting Temperature |
DSC |
10℃/min |
℃ |
133 |
|
Density |
ASTM D792 |
23℃ |
g/㎤ |
0.957 |
|
Molecular Weight Distribution |
LG Method |
GPC |
- |
Broad |
|
|
Mechanical |
Method |
Condition |
Unit |
Value |
|
Tensile Strength at Yield |
ASTM D638 |
50mm/min |
kg/㎠
MPa
psi |
310
30.6
4408.2 |
|
Elongation at Break |
ASTM D638 |
50mm/min |
% |
600 |
|
Flexural Modulus |
ASTM D790 |
2.8mm/min |
kg/㎠
MPa
psi |
14000
1381.8
199080.0 |
|
Izod Impact Strength(notched) |
ASTM D256 |
1/4″,23℃ |
kg·cm/cm
J/m
ft·lb/in |
25
245.0
4.6 |
|
Hardness |
ASTM D2240 |
Shore D |
- |
64 |
|
ESCR(F50) |
ASTM D1693 |
- |
hr |
50 |
|
|
Thermal |
Method |
Condition |
Unit |
Value |
|
Heat Deflection Temperature |
ASTM D648 |
1/2″,4.6kg/㎠ |
℃
℉ |
73
163.4 |
|
Vicat Softening Point |
ASTM D1525 |
1kg |
℃
℉ |
130
266.0 |
|
Coefficient of Liner Thermal Expansion |
ASTM D696 |
20~80℃ |
1/K |
1E-4~2.5E-4 |
|
Specific Heat |
Calorimetric |
23℃ |
cal/g·℃ |
3000 |
|
Calorimetric |
100℃ |
cal/g·℃ |
2800 |
|
| |